ASTM A738/A738M-03a
Historical Standard: ASTM A738/A738M-03a Standard Specification for Pressure Vessel Plates, Heat-Treated, Carbon-Manganese-Silicon Steel, for Moderate and Lower Temperature Service
SUPERSEDED (see Active link, below)
ASTM A738 / A738M
1. Scope
1.1 This specification covers heat-treated carbon-manganese-silicon steel plates intended for use in welded pressure vessels at moderate and lower temperature service.
1.2 Material under this specification is available in three strength levels, 75 ksi [515 MPa], 85 ksi [585 MPa], and 80 ksi [550 MPa], minimum ultimate tensile strengths.
1.3 The maximum thickness of Grade A plates is limited only by the capacity of the chemical composition and heat treatment to meet the specified mechanical property requirements. The maximum thickness of Grade B plates is limited to 2.5 in. [65 mm]. The maximum thickness of Grade C is limited to 6 in.
1.4 Grade A is the material that, prior to 1984, was covered by Specification A738 without a grade designation.
1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standards. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.
2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.
ASTM Standards
A20/A20M Specification for General Requirements for Steel Plates for Pressure Vessels
Keywords
pressure-containing parts; pressure vessel steel; steel plates; steel plates for pressure vessel applications;
ICS Code
ICS Number Code 77.140.30 (Steels for pressure purposes)